Effect of novel pre-sintered zirconia surface treatment on shear bond strength between zirconia and veneering porcelain compared to conventional surface treatments: an in-vitro study / Efeito de um novo tratamento de superfície de zircônia pré-sinterizada na resistência ao cisalhamento entre zircônia e porcelana em comparação com os tratamentos de superfície convencionais: estudo in vitro

Objective: to evaluate the effect of novel zirconia surface treatment method on shear bond strength between zirconia and veneering porcelain compared to air abrasion and CoJet surface treatment methods. Material and Methods: twenty-one zirconia ceramic discs were fabricated with diameter of 7mm and 3mm thickness and divided according to surface treatment into three subgroups, control group I: Air Abrasion (n=7), group II: CoJet (n=7) and group III: Z-etch (n=7). Porcelain was built over the zirconia specimens with a customized mold and fired in a ceramic furnace. All specimens were thermocycled (20000 cycles) between 5°C ­ 55 °C with a dwell time of 30 seconds in distilled water and shear bond strength of veneering porcelain to each zirconia specimen was tested using a universal testing machine. Results: numerical data were explored for normality by checking the distribution of data and using tests of normality (Kolmogorov-Smirnov and Shapiro-Wilk tests). One-way ANOVA test was used to compare between the groups. There was a statistically significant difference between the three groups (P-value = 0.002, Effect size = 0.503). Pair-wise comparisons between groups revealed that Z-etch showed the statistically significantly highest mean shear bond strength. Conclusion: zirconia coating using z-etch is showing promising results in promoting higher bond strength than conventional surface treatment methods as air abrasion and silica coating (AU)

Objetivo: avaliar o efeito do novo método de tratamento de superfície de zircônia na resistência ao cisalhamento entre a zircônia e a porcelana de cobertura em comparação com os métodos de abrasão a ar e jateamento com CoJet. Material e Métodos: vinte e um discos de zircônia foram confeccionados com diâmetro de 7mm e espessura de 3mm e divididos de acordo com o tratamento de superfície em três subgrupos, grupo controle I: Abrasão a ar (n=7), grupo II: CoJet (n=7) e grupo III: Z-etch (n=7). A porcelana foi aplicada sobre os espécimes de zircônia com um molde personalizado e sinterizada em forno de cerâmica. Todos os espécimes foram termociclados (20.000 ciclos) entre 5°C - 55°C com um tempo de permanência de 30 segundos em água destilada e a resistência ao cisalhamento da porcelana de cobertura foi testada através de uma máquina de ensaio universal. Resultados: os dados numéricos foram avaliados quanto à normalidade, verificando a distribuição dos dados e utilizando testes de normalidade (testes de Kolmogorov-Smirnov e Shapiro-Wilk). O teste ANOVA de um fator foi utilizado para comparar os grupos. Houve uma diferença estatisticamente significativa entre os três grupos (P-valor = 0,002, tamanho do efeito = 0,503). As comparações pareadas entre os grupos revelaram que o Z-etch apresentou a resistência de união ao cisalhamento estatisticamente significativamente mais alta. Conclusão: o revestimento de zircônia utilizando Z-etch mostrou resultados promissores para o aumento da resistência de união em comparação aos métodos convencionais de tratamento de superfície, como abrasão a ar e revestimento de sílica (AU)

Interplay between resin cements and surface-treated Poly-Ether-Ether-Ketone (PEEK): effect of aging

Aim: This study assessed the effect of thermal aging on the interfacial strength of resin cements to surface-treated PEEK. Methods: Ninety-six PEEK blocks were allocated into 4 groups (n=24), according to following surface treatments: SB - sandblasting with aluminum oxide; SA - acid etched with 98% sulfuric acid; CA ­ coupling agent (Visio.link, Bredent) and CO - control group (untreated). Surface roughness (Ra) was measured and one cylinder (1-mm diameter and height) of Rely-X Ultimate - ULT (3M/ESPE) and another one of Panavia V5 - PAN (Kuraray) were constructed on the treated or untreated PEEK surfaces. Half of the samples of each group were thermal aged (1,000 cycles). Samples were tested at a crosshead speed of 1 mm/min in shear mode (µSBS). Ra and µSBS data were compared using one- and three-way ANOVA, respectively, and Tukey's tests. Results: SA and SB samples had the roughest surfaces, while CA the smoother (p<0.001). Thermal aging reduced µSBS regardless the surface treatment and resin cement used. There was interaction between surface treatment and resin cement (p <0.001), with ULT showing higher µSBS values than PAN. SA provided higher µSBS than SB for both resin cements, while for CA µSBS was higher (PAN) or lower than SB (ULT). Conclusion: Aging inadvertently reduces interfacial strength between PEEK and the resin cements. If ULT is the resin cement of choice, reliable interfacial strength is reached after any PEEK surface treatment. However, if PAN is going to be used only SA and CA are recommended as PEEK treatment

Do irrigation solutions used during root canal instrumentation influence the adhesion of glass fiber posts? A systematic review / As soluções de irrigação usadas durante a instrumentação do canal radicular influenciam a adesão de pinos de fibra de vidro? Uma revisão sistemática

Statement of problem: the bond strength between adhesive cement and root dentin can be affected by irrigation protocols. Purpose: therefore, the objective of this systematic review was to answer the following question: Do irrigation solutions used during root canal instrumentation influence the adhesion of glass fiber posts to root dentin? Material and Methods: this study followed the recommendations of PRISMA 2020 for writing. PubMed, Scopus, Web of Science, and LILACS databases were searched for articles published until 26 January, 2022. Grey literature and a manual search were also performed. The inclusion criteria were based on the PICO strategy: permanent human or animal teeth (P), which were irrigated during root canal instrumentation with endodontic substances (I) and compared to irrigation with sodium hypochlorite at various concentrations (C) to analyze the bond strength of glass fiber posts (O). Two authors independently performed data extraction and the risk of bias. Results: eight articles were included. Four articles were classified as having a high risk of bias, where the others as medium risk. Studies have reported conflicting results regarding the influence of irrigating solutions and the different concentrations of sodium hypochlorite on the adhesion of glass fiber posts to root dentin. Conclusion: the heterogeneity between studies did not allow the conclusion of a true estimate regarding this topic, and further well-designed studies are needed to clarify this issue. Register: CRD42020221835. (AU)

Definição do problema: a resistência de união entre o cimento adesivo e a dentina radicular pode ser afetada pelos protocolos de irrigação. Objetivo: portanto, o objetivo desta revisão sistemática foi responder à seguinte questão: As soluções de irrigação usadas durante a instrumentação do canal radicular influenciam a adesão de pinos de fibra de vidro à dentina radicular? Material e Métodos: este estudo seguiu as recomendações do PRISMA 2020 para sua redação. As bases de dados PubMed, Scopus, Web of Science e LILACS foram pesquisadas para artigos publicados até 26 de janeiro de 2022. A literatura cinza e uma pesquisa manual também foram realizadas. Os critérios de inclusão foram baseados na estratégia PICO: dentes humanos ou animais permanentes (P), que foram irrigados durante a instrumentação do canal radicular com substâncias endodônticas (I) e comparados à irrigação com hipoclorito de sódio em várias concentrações (C) para analisar a resistência de união de pinos de fibra de vidro (O). Dois autores realizaram independentemente a extração de dados e o risco de viés. Resultados:oito artigos foram incluídos. Quatro artigos foram classificados como de alto riscode viés, enquanto os demais como de médio risco. Estudos relataram resultados conflitantes sobre a influência de soluções irrigadoras e as diferentes concentrações de hipoclorito de sódio na adesão de pinos de fibra de vidro à dentina radicular. Conclusão: a heterogeneidade entre os estudos não permitiu a conclusão de uma estimativa verdadeira sobre este tópico, sendo necessários mais estudos bem delineados para esclarecer esta questão. Registo: CRD42020221835 (AU)

Influência da adição de partículas de vidro bioativas em adesivos resinosos, na cimentação de bráquetes ortodônticos / Influence of the addition of bioactive glass particles in resin adhesives in the cementation of orthodontic brackets

O objetivo deste estudo foi desenvolver e avaliar um adesivo resinoso modificado com a incorporação de partículas de vidro bioativas (SCHOTT Bioactive Glass) em diferentes concentrações. Foram avaliados a resistência ao cisalhamento (RU), o índice de remanescente dentário (IRA), o grau de conversão (GC) e a liberação de cálcio. Foram utilizados 50 incisivos bovinos que foram fixados, através de suas raízes, em um molde de PVC, com resina acrílica autopolimerizável. As amostras foram alocadas em 5 grupos (n=10): TXT - Adesivo Transbond XT (3M Unitek, Monrovia, CA, EUA) sem adição de partículas de vidro bioativas, TXT20, TXT30, TXT50 ­ Adesivo Transbond XT acrescido respectivamente de 20%, 30% e 50% de partículas de vidro bioativas e SH - Adesivo resinoso FL BOND ll (SHOFU Inc.) com biomaterial SPRG. As amostras receberam uma profilaxia com pedra pomes e condicionamento com ácido fosfórico à 37%. Em seguida foi aplicada uma fina camada do sistema adesivo indicado na face vestibular dos incisivos bovinos, em todos os grupos e fotopolimerizado por 20 segundos, utilizando-se um fotopolimerizador RADII-Cal (SDI, Victoria, Austrália). Depois foi aplicada uma pequena quantidade de pasta resinosa fotopolimerizável Transbond XT (3M Unitek, Monrovia, CA, EUA) sobre a superfície dos bráquetes autoligados (MORELLI, Sorocaba, São Paulo, Brasil) e estes foram devidamente colados na face vestibular, no centro da coroa clínica do incisivo bovino e fotopolimerizado por 20 segundos, em cada face. Posteriormente as amostras foram submetidas ao teste de resistência ao cisalhamento. O índice de remanescente adesivo foi avaliado em estereomicroscópio DISCOVERY V20 (ZEISS). Os adesivos resinosos foram submetidos ao teste de grau de conversão e liberação de cálcio. Os dados foram inicialmente submetidos ao teste de normalidade e depois submetidos ao teste de ANOVA um fator, seguido do teste de Tukey para análise de comparações múltiplas, com nível de significância de 0,05. De acordo com os resultados obtidos na resistência de união ao cisalhamento (MPa±Dp) a maior média foi observada no grupo TXT 19,50±1,40A, seguida do grupo TXT20 18,22±1,04AB, seguida do grupo SH 17,62±1,45B, seguida do grupo TXT30 14,48±1,46C e a menor média TXT50 14,13±1,02C. No grau de conversão a maior média foi observada no grupo TXT20 73,02±3,33A que foi estatisticamente semelhante ao grupo SH 68,50±1,09A, seguida do grupo TXT 60,28±1,06B e TXT30 58,84±4,06B e a menor média foi do grupo TXT50 40,67±1,21C.Para a liberação de cálcio a maior média foi TXT50 2,23±0,11D, seguida por TXT30 0,74±0,00C, TXT20 0,55±0,00B, SH 0,47±0,04B e TXT 0,14±0,00A. Concluiu-se que a incorporação de partículas de vidro bioativas influenciou na resistência de união ao cisalhamento, no grau de conversão e na liberação de cálcio (AU).

The objective of this study was to develop and evaluate a resin adhesive modified with the incorporation of bioactive glass particles (SCHOTT Bioactive Glass) in different concentrations. Shear bond strength (SBS), adhesive remnant index (ARI), degree of conversion (DC) and calcium release were evaluated. Fifty bovine incisors were used, which were fixed through their roots in a PVC mold with self-curing acrylic resin. The samples were allocated into 5 groups (n=10): TXT ­ Transbond XT Adhesive (3M Unitek, Monrovia, CA, USA) without addition of bioactive glass particles, TXT20, TXT30, TXT50 ­ Transbond XT Adhesive rescpectively increased by 20%, 30% and 50% bioactive glass particles and SH ­ FL BOND ll resin adhesive (SHOFU Inc.) with SPRG biomaterial. The samples received prophylaxis with pumice stoe and conditioning with 37% phosphoric acid. Then, a thin layer of the indicated adhesive system was applied to the buccal surface of the bovine incisors, in all groups, and light cured for 20 seconds, using a RADII-Call curing light (SDI, Victoria, Australia). Then, a small amount of Transbond XT light-curing resinous paste (3M Unitek, Monrovia, CA, USA) was applied on the surface of the self-ligating brackets (MORELLI, Sorocaba, São Paulo, Brazil) and these were duly bonded on the buccal surface, in the center of the clinical crown of the bovine incisor and light cured for 20 seconds, on each side. Subsequently, the samples were submitted to the shear bond test. The adhesive remnant index was evaluated using a DISCOVERY V20 stereomicroscope (ZEISS). The resin adhesives were submitted to the degree of conversion and calcium release test. The data were initially submitted to the normality test and then submitted to the one-way ANOVA test, followed by the Tukey test for analysis of multiple comparisons, with a significance level of 0.05. According to the results obtained in the shear bond strength (MPa±Dp), the highest average was observed in the TXT group 19.50±1.40A, followed by the TXT20 group 18.22±1.04AB, followed by the SH group 17.62±1.45B, followed by the TXT30 group 14.48±1.46C and the lowest mean TXT5014.13±1.02C. In the degree of conversion, the highest average was observed in the TXT20 73.02±3.33A group, wich was statiscally like the SH group 68.50±1.09A, followed by the TXT 60.28±1.06B and TXT30 group 58.84±4.06B and the lowest mean was for the TXT50 group 40.67±1.21C. For calcium release, the highest mean was TXT50 2.23±0.11D, followed by TXT30 0.74±0.00C, TXT20 0.55±0.00B, SH 0.47±0.04B and TXT 0.14±0.00A. It was concluded that the incorporation of bioactive glass particles influenced in the shear bond strength, in the degree of conversion and in the release of calcium (AU).

Comparison of shear bond strength and color reproduction of two different high-performance polymers veneered with two different thicknesses of resin composite: an in-vitro study / Comparação da resistência ao cisalhamento e reprodução de cor de dois diferentes polímeros de alto desempenho revestidos com duas diferentes espessuras de resina composta: um estudo in vitro

Objective: to evaluate the effect of material type and veneer thickness on the final color and shear bond strength of PEEK bilayered restorations. Material and Methods: sixty-four square-shaped core specimens (7×7×2), were fabricated by CAD/CAM technology from two high-strength polymers, BioHPP (High-Performance Polymer, group B n=32), and Pekkton® ivory (PolyEtherKetoneKetone, group P n=32) then were veneered with resin composite (crea.lign dentin A3). Specimens from each group were divided (n=16) according to the veneer layer thickness (0.5 & 1 mm), then according to the test applied (n=8), either ΔE or shear bond strength (SBS). Specimen surfaces were treated according to the manufacturer's instructions. Specimens were veneered according to the manufacturer's instructions.The mode of failure was evaluated under a stereomicroscope at 40 x magnification after the shear bond strength test. Results: data showed parametric distribution and variance homogeneity and were analyzed using two-way ANOVA. The significance level was set at p<0.05 for all tests. Statistical analysis was performed with the R statistical analysis software version 4.3.1.Results of two-way ANOVA showed that material types and veneer thicknesses had an individual significant effect on the color change. For the shear bond strength, only the sample thickness (1mm) had a significant effect (p=0.033). The majority of samples in different groups presented a mixed failure mode with all the differences being not statistically significant (p>0.05). Conclusion: the thickness of the resin composite veneer can significantly affect the final esthetic outcome and shear bond strength of a bilayered restoration.(AU)

Objetivo: avaliar o efeito do tipo de material e da espessura do revestimento na cor final e na resistência ao cisalhamento de restaurações em duas camadas de PEEK. Material e Métodos: foram fabricados 64 espécimes com núcleo de formato quadrado (7x7x2) usando tecnologia CAD/CAM a partir de dois polímeros de alta resistência, BioHPP (Polímero de Alto Desempenho, grupo B n=32) e Pekkton ivory (Polieterecetona cetona, grupo P n=32), que foram então revestidos com resina composta (crea.lign dentin A3). Os espécimes de cada grupo foram divididos (n=16) de acordo com a espessura do revestimento (0,5 e 1 mm), e depois de acordo com o teste aplicado (n=8), seja ΔE ou resistência ao cisalhamento (SBS). As superfícies dos espécimes foram tratadas de acordo com as instruções do fabricante. Os espécimes foram revestidos de acordo com as instruções do fabricante. O modo de falha foi avaliado sob um estereomicroscópio com ampliação de 40x após o teste de resistência ao cisalhamento. Resultados: os dados apresentaram distribuição paramétrica e homogeneidade de variância e foram analisados por ANOVA de duas vias. O nível de significância foi estabelecido em p<0,05 para todos os testes. A análise estatística foi realizada com o software de análise estatística R, versão 4.3.1. Os resultados da ANOVA de duas vias mostraram que os tipos de materiais e as espessuras do revestimento tiveram um efeito significativo individual na mudança de cor. Para a resistência ao cisalhamento, apenas a espessura da amostra (1mm) teve um efeito significativo (p=0,033). A maioria das amostras em diferentes grupos apresentou um modo de falha misto, com todas as diferenças não sendo estatisticamente significativas (p>0,05). Conclusão:a espessura do revestimento de resina composta pode afetar significativamente o resultado estético final e a resistência ao cisalhamento de uma restauração em duas camadas.(AU)

Effect of adhesive primer application on shear bond strength of self-adhesive cement to tooth structure and two different CAD/CAM milled blocks / Efeito da aplicação do primer adesivo na resistência ao cisalhamento do cimento autoadesivo à estrutura dentária e a dois diferentes blocos fresados CAD/CAM

Objective: This study was conducted to evaluate the influence of the G-CEM ONE adhesive enhancing primer on the shear bond strength of self-adhesive resin cement (G-CEM ONE) to both tooth structure and two different CAD/CAM blocks (GC Initial LiSi and Cerasmart 270). Material and Methods: Forty specimens (cylindrical-shaped, 5 mm in diameter and height) were milled from both CAD/CAM blocks (20 specimens from each block type). Forty sound upper premolars were sectioned to the level of peripheral dentin, then randomly divided into four groups (n = 10): A1: GC Initial LiSi without adhesive enhancing primer; B1: Cerasmart 270 without adhesive enhancing primer; A2: GC Initial LiSi with adhesive enhancing primer; B2: Cerasmart 270 group with adhesive enhancing primer application. The CAD/CAM blocks were cemented on teeth using a self-adhesive resin cement (G-cem one). The shear bond strength was assessed using a computerized universal testing machine. A digital microscope was used to study the mode of failure. The shear bond strength values data were analyzed statistically using paired t-test and independent t-test at the significance level of (0.05). Results: A significant difference was shown in the shear bond strength values among groups (P =0.000). The highest shear bond strength value was revealed in group A2, while group B1 exhibited the lowest shear bond strength value. Conclusion: Using the adhesive enhancing primer on the tooth's surface improved the resin cement's bond strength to CAD/CAM blocks. Additionally, GC Initial LiSi exhibited higher bond strength than Cerasmart 270, with or without the primer (AU)

Objetivo: Este estudo foi conduzido para avaliar a influência do primer adesivo G-CEM ONE na resistência ao cisalhamento do cimento resinoso autoadesivo (G-CEM ONE) tanto na estrutura dentária quanto em dois diferentes blocos CAD/CAM (GC Initial LiSi e Cerasmart 270). Material e Métodos: Quarenta corpos de prova (formato cilíndrico, 5 mm de diâmetro e altura) foram fresados em blocos CAD/CAM (20 corpos de prova de cada tipo de bloco). Quarenta pré-molares superiores sadios foram seccionados até o nível da dentina mais externa e, em seguida, divididos aleatoriamente em quatro grupos (n = 10): A1: GC Initial LiSi sem primer adesivo; B1: Cerasmart 270 sem primer adesivo; A2: GC Initial LiSi com primer adesivo; B2: Grupo Cerasmart 270 com aplicação de primer adesivo. Os blocos CAD/CAM foram cimentados nos dentes com cimento resinoso autoadesivo (G-CEM ONE). A resistência ao cisalhamento foi avaliada utilizando uma máquina de ensaios universal computadorizada. Um microscópio digital foi utilizado para estudar o modo de falha. Os dados dos valores de resistência ao cisalhamento foram analisados estatisticamente por meio do teste t pareado e teste t independente ao nível de significância de (0,05). Resultados: Foi demonstrada diferença significativa nos valores de resistência ao cisalhamento entre os grupos (P =0,000). O maior valor de resistência ao cisalhamento foi revelado no grupo A2, enquanto o grupo B1 exibiu o menor valor de resistência ao cisalhamento. Conclusão:A utilização do primer adesivo na superfície dentária melhorou a resistência de união do cimento resinoso aos blocos CAD/CAM. Além disso, o GC Initial LiSi apresentou maior resistência de união que o Cerasmart 270, com ou sem primer.(AU)

Effect of time and dental substrate on the bond strength of a universal adhesive system: in vitro study / Efeito do tempo e do substrato dental na resistência de união de um sistema adesivo universal: estudo in vitro

Introduction: Dentin adhesives provide union between the dental substrate and composite resin, but this union can be influenced by the cleaning agent. Objective: Evaluate the use of ozonated water as a cavity cleaning solution. Material and method: 40 bovine dental crowns were selected, divided into four groups: AD (dentin cleaning with distilled water) and AO (dentin cleaning with ozonized distilled water). Each group was divided into two storage periods (24h and 30 days) kept at 37 °C. The selected universal system adhesive was employed according to the manufacturer's instructions and light cured for 20 seconds. At that time, three cylinders were made (Tygon matrix with an internal diameter of 2 mm and a height of 2 mm) of composite resin in the crowns in the cervical, médium, and incisal regions and light cured for 30 seconds. After storage, the bonding strength was tested by micro-shear, and fracture type analysis was performed. The data were submitted to statistical analysis using the Shapiro-Wilk test with a significance level of 95%, ANOVA, and Turkey. Result: There was a statistically significant difference between the bond strength values, only in the intergroup analysis for the time of 24 hours, between the middle third of the groups (LDAO24 = 2.70 (± 2.39); LDAO30 = 3.82 (± 2.31)). The predominant fracture type for both groups was an adhesive fracture, except in the medium and incisal thirds of the AD, which was a cohesive dentin fracture. Conclusion: The utilization of ozone did not change the bond strength adhesive.

Introdução: Os adesivos dentinários proporcionam união entre o substrato dental e resina composta, porém esta união pode ser influenciada pelo agente de limpeza. Objetivo: Avaliar a influência na resistência de união (RU) de um sistema adesivo universal associado à da água ozonizada como solução de limpeza cavitária. Material e método: Foram selecionadas 40 coroas de dentes anteriores bovinos divididos em 4 grupos: AD (limpeza dentinária com água destilada) e AO (limpeza dentinária com água destilada ozonizada). Cada grupo foi subdividido em outros dois grupos de acordo com o tempo de armazenamento (24h e 30 dias) armazenados a 37ºC. A limpeza dentinária foi realizada por meio de uma seringa de 60mL de cada solução e fricção por 10 segundos. O sistema adesivo universal selecionado foi aplicado de acordo com as instruções do fabricante e fotoativado por 20 segundos. Em seguida, foram confeccionados 3 cilindros (matriz Tygon com um diâmetro interno de 2 mm e 2 mm de altura) de resina composta nas coroas nas regiões cervical, média e incisal e fotoativados por 30 segundos. Após o armazenamento foi realizado o teste de RU por microcisalhamento e análise do tipo de fratura. Os dados coletados foram submetidos a análise estatística através do teste de Shapiro Wilk com nível de significância de 95%, ANOVA e Tukey. Resultado: Houve diferença estatística significativa entre os valores de RU apenas na análise intergrupos para o tempo de 24 horas, entre o terço médio dos grupos (LDAO24 = 2,70 (± 2,39); LDAO30 = 3,82 (± 2,31)). O tipo de fratura predominante para ambos os grupos em todos os tempos foi de fratura adesiva, com exceção ao terço médio e incisal do AD, que foi fratura coesiva de dentina. Conclusão: A utilização do ozônio não alterou a resistência de união adesiva.

Influence of etching Mode and composite type on bond strength to biodentine using a ''No-Wait'' universal adhesive / Influencia del modo de grabado y del tipo de resina en la resistencia adhesiva al Biodentine utilizando un adhesivo universal tipo "no-wait"

Abstract: The purpose of this study was to compare the shear bond strength (SBS) of four resin-based composite materials to a silicate-based cement using a ''no-wait'' universal bond with self-etch (SE) and etch-and-rinse (ER) modes. Acrylic blocks (n=80, 2mm depth, 5mm diameter central hole) were prepared. The holes were filled with BiodentineTM (BD) and divided into 4 main groups (n=20) according to the composite resin type used: Group FZ250: FiltekTM Z250 Universal Restorative (microhybrid), Group SDR: SDR Plus U Bulk Fill Flowable (low-viscosity bulk-fill), Group FBP: FiltekTM Bulk Fill Posterior (high-viscosity bulk-fill), Group EF: EsFlow™ Universal Flowable Composite (nanohybrid). A 'no-wait' universal bond (Clearfil Universal Bond Quick) was used for bonding application. Then each group was divided into 2 subgroups according to the etching mode applied (ER and SE). SBSs were measured and stereomicroscope was used to identify the failure modes. Selected samples of fracture surfaces were imaged by SEM. Tukey's post-hoc and One-way ANOVA tests were used to analyze data. There were statistically significant differences among the composite groups (p 0.05). The SBS of BD to the resin composites depends on the composite type but application of the 'no-wait' universal bond in different etching modes is regardless of the SBS of BD to resin composites.

Resumen El objetivo de este estudio fue comparar la resistencia de adhesión al cizallamiento (SBS) de cuatro resinas con un cemento a base de silicato utilizando una adhesivo universal "no-wait" de autograbado (SE) y grabado y lavado (ER). Se prepararon bloques acrílicos (n=80, de 2mm de profundidad y un agujero central de 5mm de diámetro). Los agujeros se rellenaron con BiodentineTM (BD) y se dividieron en 4 grupos principales (n=20) según el tipo de resina compuesta utilizada: Grupo FZ250: FiltekTM Z250 Universal Restorative (microhíbrido), Grupo SDR: SDR Plus U Bulk Fill Flowable (bulk-fill de baja viscosidad), Grupo FBP: FiltekTM Bulk Fill Posterior (bulk-fill de alta viscosidad), Grupo EF: EsFlow™ Universal Flowable Composite (nanohíbrido). Para la aplicación de la adhesión se utilizó un adhesivo universal "no-wait" (Clearfil Universal Bond Quick). A continuación, cada grupo se dividió en 2 subgrupos según el modo de grabado aplicado (ER y SE). Se midieron los SBS y se utilizó el estereomicroscopio para identificar los modos de fallo. Las muestras seleccionadas de las superficies de fractura se analizaron mediante SEM. Se utilizaron las pruebas post-hoc de Tukey y ANOVA de una vía para analizar los datos. Hubo diferencias estadísticamente significativas entre los grupos de composites (p0,05). La SBS de la BD a los composites de resina depende del tipo de composite, pero la aplicación de la unión universal "no-wait" en los diferentes modos de grabado es independiente de la SBS de la BD a los composites de resina.

Evaluation of dentin microroughness and composite bond strength after multiple uses of diamond burs / Evaluación de la micro rugosidad dentinaria y la resistencia adhesiva de composites tras múltiples usos de fresas de diamante

Abstract Using a bur multiple times to prepare dental structure may produce a smoother final surface on dentin than a new one. This superficial roughness may affect adhesion with resin-based materials by modifying the substrates' characteristics. The aim of this study was to evaluate the effect of multiple uses of diamond burs on dentin's superficial microroughness and bond strength with resin composite when using a self-etch adhesive. Diamond dental burs were used to simulate a preparation (dentin flat surface) on extracted third molars. Samples were distributed into groups according to burs' number of previous uses as follows: 0, 1, 5 and 10. Scanning electron microscopy images at 70x, 350x, and 1000x were used to illustrate burs' deformation. Each specimen's dentin microroughness was measured three times to compare between experimental groups and the micro-shear bond strength test (n=15) was performed for the 0 and 10 uses groups using a universal adhesive in a self- etching mode. Diamond crystals wear and dislodgements were evident among groups where the burs were used more times. As the number of uses increased the mean microroughness of the dentin surface decreased with significant differences between the 0 and 10 uses groups. No statistical differences between experimental groups resulted from bond strength tests. When using a universal adhesive in a self-etching mode, the number of previous uses of a diamond bur seems to have no significant effect on dentin/resin composite bond strength.

Resumen El uso de una fresa múltiples veces para preparar la estructura dental puede producir una superficie final más lisa en la dentina que una fresa nueva. Esta rugosidad superficial modifica las características del sustrato y puede afectar la adhesión con materiales resinosos. El objetivo de este estudio fue evaluar el efecto de los múltiples usos de las fresas de diamante sobre la micro rugosidad superficial de la dentina y la resistencia adhesiva con la resina compuesta cuando se utiliza un adhesivo de autograbado. Se utilizaron fresas dentales de diamante para simular una preparación (superficie plana de la dentina) en terceros molares extraídos. Las muestras se distribuyeron en grupos según el número de usos previos de las fresas de la siguiente manera: 0, 1, 5 y 10. Se utilizaron imágenes de microscopía electrónica de barrido a ×70, ×350 y ×1000 para ilustrar la deformación de las fresas. Se midió la micro rugosidad de la dentina de cada espécimen tres veces para comparar entre los grupos experimentales y se realizó la prueba de resistencia a la adhesión por micro cizallamiento (n=15) para los grupos de 0 y 10 usos utilizando un adhesivo universal en modo de autograbado. El desgaste de los cristales de diamante y los desprendimientos fueron evidentes entre los grupos en los que las fresas se utilizaron más veces. A medida que aumentaba el número de usos, la micro rugosidad media de la superficie de la dentina disminuyó, con diferencias significativas entre los grupos de 0 y 10 usos. En las pruebas de resistencia adhesiva no se observaron diferencias estadísticas entre los grupos experimentales. Cuando se utiliza un adhesivo universal en modo de autograbado, el número de usos previos de una fresa de diamante no parece tener un efecto significativo en la resistencia de la unión dentina/resina del composite.

Adhesion of a sealant with pre-reacted glass ionomer particles under salivary contamination: an in vitro study

Objective: this in vitro study compared the adhesive strengths of the resin sealant with the Giomer technology sealant under salivary contamination. Materials and Methods: fifty-two bovine incisors were randomly divided into four groups (n=13): GI, a resin sealant (Fluroshield®) without salivary contamination (control of GII); GII, Fluroshield sealant + salivary contamination; GIII, a Giomer technology sealant (BeautiSealant®) without salivary contamination (control of GIV); and GIV, BeautiSealant® sealant + salivary contamination. In the salivary contamination groups, artificial saliva was used through a pipette, and after 20 s, it was air-dried and the sealant was applied. Shear strength tests were performed using a universal testing machine. One-way ANOVA variance and Tukey's test were used for multiple comparisons. The fracture types were analyzed using a stereomicroscope with 40X magnification. Results: the means and standard deviations (SD) of adhesion for Fluroshield® and BeautiSealant® in the group without salivary contamination were 15.27 (±0.96) and 11.90 (±0.94), and for the group with salivary contamination, 13.14 (±1.03) and 8.95 (±1.33), respectively, indicating a statistically significant difference between GI and GII p=0.020, GIII and GIV p=0.041. Mixed failures were detected in GI (38%), GII (44%), GIII (38%), and GIV (62%). Conclusion: there was a statistically significant decrease in the adhesive strength values in the groups with salivary contamination for both the sealants studied. However, no significant difference was observed between the two sealants when the materials used were compared.

Objetivo: este estudo in vitro comparou as forças adesivas do selante resinoso com o selante da tecnologia Giomer sob contaminação salivar. Materiais e Métodos: cinquenta e dois incisivos bovinos foram divididos aleatoriamente em quatro grupos (n=13): GI, um selante resinoso (Fluroshield®) sem contaminação salivar (controle do GII); GII, selante Fluroshield + contaminação salivar; GIII, um selante com tecnologia Giomer (BeautiSealant®) sem contaminação salivar (controle do GIV); e GIV, selante BeautiSealant® + contaminação salivar. Nos grupos de contaminação salivar, a saliva artificial foi utilizada por meio de uma pipeta e, após 20 s, foi seca ao ar e aplicado o selante. Os testes de resistência ao cisalhamento foram realizados usando uma máquina de teste universal. A variância ANOVA de uma via e o teste de Tukey foram usados para comparações múltiplas. Os tipos de fratura foram analisados em estereomicroscópio com aumento de 40X. Resultados: as médias e desvios padrão (DP) de adesão para Fluroshield® e BeautiSealant® no grupo sem contaminação salivar foram 15,27 (±0,96) e 11,90 (±0,94), e após contaminação salivar foram 13,14 (±1,03) e 8,95 (±1,33), respectivamente, indicando haver diferença estatisticamente significante entre GI e GII p=0.020, GIII e GIV p=0.041. Falhas mistas foram detectadas em GI (38%), GII (44%), GIII (38%) e GIV (62%). Conclusão: houve diminuição estatisticamente significativa dos valores de resistência adesiva nos grupos com contaminação salivar para ambos os selantes estudados. No entanto, não foi observada diferença significativa entre os dois selantes quando comparados os materiais utilizados.

The efficiency of ErCr: YSGG laser on the debonding of different thicknesses of ceramic veneers

Aims: To verify the efficacy of Er,Cr:YSGG laser for debonding of lithium disilicate (LD) reinforced glass ceramic veneers of different thicknesses. Methods: Forty bovine teeth were prepared and randomly divided into four groups (n=10/group) according to the ceramic disc thickness: C0.5 (Control group) and L0.5 (Laser irradiated group) in which LD discs had a thickness of 0.5mm and 5mm diameter; C1 and L1 in which LD discs had a thickness of 1mm and 5mm diameter. The lithium disilcate discs (IPS E.max®, shade HTA2) were fabricated following the manufacturer's recommendations and cemented to the prepared tooth surface. The Er,Cr:YSGG laser was applied to the laser groups at 2.5W and 25Hz for 60seconds. Universal testing machine was used to evaluate the shear bond strength for all samples at a cross head speed of 1mm/min in an inciso-gingival direction parallel to the sample surface. After debonding, the samples were examined under stereoscope to evaluate the mode of failure according to the adhesive remnant index (ARI). Results: Laser irradiation significantly diminishes the shear bond strength from 10.868 MPa to 3.778 MPa for C0.5 and L0.5 groups respectively (p=0.00) and from 14.711 MPa to 4.992 MPa for C1 and L1 groups respectively (p=0.00). The shear bond strength required for debonding increased with increasing thickness of discs, but without significant difference (p=0.110). Higher ARI scores were seen in the laser groups (more cement remaining adhered to the tooth) when compared to the control groups. Conclusions: The Er,Cr:YSGG laser could be an effective and useful tool in debonding of lithium disilicate ceramic veneers as it decreases the shear bond strength required for veneer debonding

Uso efectivo de los adhesivos de octava generación / Effective use of eighth generation adhesives

Introducción: se realizó una revisión bibliográfica con el objetivo de conocer, analizar y comparar los diferentes tipos de adhesivos de octava generación que se encuentran en el mercado y la diferencia que existe entre cada uno. Los adhesivos universales han demostrado mejoras en su resistencia, sobre todo en las técnicas de aplicación y en las propiedades de estos materiales, al mejorar la fuerza adhesiva para que el odontólogo pueda brindar tratamientos restaurativos exitosos. Objetivo: conocer, analizar y comparar los diferentes tipos de adhe- sivos de la octava generación empleados en odontología. Material y métodos: se realizó una búsqueda en las bases de datos electrónicas PubMed, BVS, Redalyc y ScienceDirect. Se utilizaron 32 artículos que cumplieron con los criterios predeterminados y la especificidad reque- rida para la pregunta de investigación. Conclusiones: se demostró que la tecnología cada día avanza, sobre todo en el área de los adhesivos, ya que éstos son de mucha utilidad en el día a día del odontólogo; es importante conocer cada uno de éstos, puesto que es un poco complejo seleccionar el correcto, mas no el uso. En la actualidad, existen diversas opciones por las que el odontólogo puede optar, es por ello que el pro- fesional debe estar capacitado sobre cada una de las diferentes marcas existentes y, de acuerdo al tratamiento, debe elegir cuál es mejor utilizar en una rehabilitación. Es importante para el odontólogo conocer estos materiales, ya que esto lo beneficiará al momento de llevar un plan de tratamiento restaurador (AU)

Introduction: a bibliographic review was carried out to learn about, analyze, and compare the different types of eighth-generation adhesives on the market and the difference between each one. Universal adhesives have demonstrated improvements in their resistance, especially in the application techniques and properties of these materials, improving the adhesive strength so that the dentist can provide successful restorative treatments. Objective: to know, analyze and compare the different types of eighth-generation adhesives used in dentistry. Material and methods: a search was made of the following electronic databases: PubMed, BVS, Redalyc, ScienceDirect. Finally, 32 articles that met the predetermined criteria and the specificity required for the research question were used. Conclusions: it was demonstrated that technology is advancing every day, especially in the area of adhesives since these are very useful in the daily life of the dentist. It is important to know each one of these since it is a little complex at the moment of selecting the correct one, but not the use. Currently, there are several options that the dentist can choose, which is why the professional must be trained on each of the various existing brands and according to the treatment which is the best to use at the time of rehabilitation. The dentist needs to know these materials since they will benefit him/her when carrying out a restorative treatment plan (AU)

Cimentação adesiva de cerâmicas vítreas para CAD/CAM: efeito do tipo de sistema adesivo e do envelhecimento em longo prazo na resistência de união ao cimento resinoso / Adhesive cementation of glass ceramics for CAD/CAM: effect of the type of adhesive system and long-term aging on the bond strength to resin cement

O objetivo desta pesquisa foi avaliar o efeito do tipo de sistema adesivo e do envelhecimento na molhabilidade e resistência de união das cerâmicas vítreas ao cimento resinoso. Blocos de silicato de lítio (SL - Celtra Duo, Dentsply Sirona), feldspática (FD - Vita Mark II, VITA Zahnfabrik) e cerâmica infiltrada por polímero (PIC - Vita Enamic, VITA Zahnfabrik) foram seccionados (N=96, 10 x 12 x 2 mm), incluídos e divididos aleatoriamente em 24 grupos de acordo com os fatores: "Cerâmica" (SL, FD e PIC), "Adesivo" (CONT­sem adesivo; C2P­ adesivo convencional de 2 passos; C3P­adesivo convencional de 3 passos; UNV­adesivo universal) e "Envelhecimento" (SE-sem; CE­com). Após o condicionamento das cerâmicas (HF 5%), silanização e aplicação do sistema adesivo de acordo com o grupo experimental, cilindros (n=15, Ø = 2 mm e altura = 2 mm) de cimento resinoso (RelyX Ultimate, 3M ESPE) foram confeccionados (4 cilindros/bloco), sendo metade das amostras armazenadas em água destilada a 37°C por 24h (SE) e metade foi submetida à termociclagem 10.000 ciclos e armazenamento em água a 37°C por 18 meses (CE). Em seguida, as amostras foram submetidas ao teste de resistência de união ao cisalhamento (RUC - 100 KgF, 1 mm/min), análises de falhas, mensuração do ângulo de contato e análise da interface por meio da microscopia eletrônica de varredura (MEV). Os dados da RUC (MPa) e ângulo de contato foram analisados pelo ANOVA2 fatores e ANOVA-1 fator, respectivamente e Tukey (5%). A análise de Weibull foi realizada para a RUC. ANOVA-2 fatores revelou que o fator "Adesivo" foi significativo apenas para as cerâmicas SL (p<0,0001) e FD (p=0,0079). Já a interação Adesivo/Envelhecimento (p=0,0015) e "Envelhecimento" (p=0,0008) foram significativos apenas para SL. Para SL, após o envelhecimento os grupos CE_UNV (22,18± 7,74CD) e CE_C2P (17,32± 5,86D ) foram inferiores ao controle (30,30± 6,11A ). Apenas o grupo UNV apresentou redução significativa após envelhecimento. Para FD, C2P apresentou a menor RUC em relação aos demais grupos. PIC apresentou similaridade da RUC entre todos os grupos. O ângulo de contato de UNV apresentou o menor valor para SL (55,27°) e FD (51,34°). Para PIC, C3P apresentou o maior ângulo (63,00°) e CONT o menor (49,83°). Portanto, a aplicação de um adesivo não foi benéfica para a adesão da cerâmica ao cimento. Ademais, o uso de C2P e UNV após silanização da cerâmica SL e C2P para FD deve ser avaliada com precaução, já que a resistência de união foi reduzida em comparação ao grupo controle após o envelhecimento (AU).

The aim of this study was to evaluate the effect of the type of adhesive system and aging on the wettability and bond strength of glass ceramics to resin cement. Lithium silicate (SL - Celtra Duo, Dentsply Sirona), feldspathic (FD - Vita Mark II, VITA Zahnfabrik) and polymerinfiltrated ceramic (PIC - Vita Enamic, VITA Zahnfabrik) blocks were sectioned (N=96, 10 x 12 x 2 mm), included and randomly divided into 24 groups according to the factors: "Ceramics" (SL, FD and PIC), "Adhesive" (CONT­without adhesive; C2P­conventional 2-step adhesive; C3P­adhesive conventional 3-step; UNV­universal adhesive) and "Aging" (SE-non-aged; CEaged). After the conditioning of the ceramics (HF 5%), silanization and application of the adhesive system according to the experimental group, cylinders (n=15, Ø = 2 mm and height = 2 mm) of resin cement (RelyX Ultimate, 3M ESPE) were made (4 cylinders/block) and half of the samples were stored in distilled water at 37°C for 24h (SE) and half were subjected to thermocycling 10,000 cycles and storage in water at 37°C for 18 months (EC). Then, the samples were submitted to the shear bond strength test (RUC - 100 KgF, 1 mm/min), failure analysis, contact angle measurement and interface analysis by means of scanning electron microscopy (SEM). RUC (MPa) and contact angle data were analyzed by ANOVA 2-way and ANOVA 1-way, respectively, and Tukey (5%). Weibull analysis was performed for RUC. ANOVA 2-way revealed that the "Adhesive" factor was significant only for SL (p<0.0001) and FD (p=0.0079) ceramics. The Adhesive/Aging interaction (p=0.0015) and "Aging" (p=0.0008) were significant only for SL. For SL, after aging, the CE_UNV (22.18± 7.74CD) and CE_C2P (17.32± 5.86D) groups were lower than the control (30.30± 6.11A). Only the UNV group showed a significant decrease after aging. For FD, C2P had the lowest RUC in relation to the other groups. PIC showed similarity of RUC between all groups. The UNV contact angle presented the lowest value for SL (55.27°) and FD (51.34°). For PIC, C3P presented the highest angle (63.00°) and CONT the smallest (49.83°). Therefore, the application of an adhesive was not beneficial for the adhesion of the ceramic to the resin cement. Furthermore, the use of C2P and UNV after silanization of SL and C2P ceramics for FD should be evaluated with caution, as the bond strength was reduced compared to the control group after aging (AU).

Influence of ceramic primers on microshear bond strength to zirconia

This study aimed to investigate the effect of two ceramic primers on the microshear bond strength (µSBS) of yttria-stabilized zirconia (Y-TZP) to two types of self-adhesive resin cement and one BisGMA-based resin cement. Zirconia specimens were sandblasted with 27-µm aluminum oxide and composite cylinders were cemented with resin cement with or without the prior use of ceramic primers. Nine groups (n=12) were randomly distributed according to the cement (self-adhesive RelyX U200/3M ESPE, self-adhesive Maxcem Elite/Kerr, and BisGMA-based dual-cure RelyX ARC/3M ESPE) and ceramic primer (Z-Primer Plus/Bisco and Porcelain Liner M/Sun Medical Co.). After luting, the specimens were stored in distilled water at 37°C for 24 hours and then submitted to the µSBS test. The data were analyzed with two-way ANOVA followed by the Scheffe post hoc test (p<0.05). There were significant differences between RelyX U200 and other groups. There were also significant differences between the RelyX U200 group without ceramic primer and other groups without ceramic primers (p<0.05). Self-adhesive resin cement (RelyX U200 and MaxCem) presented higher microshear bond strength (6.17 and 2.32 MPa) than the conventional resin cement (RelyX ARC) when a porcelain primer was not used (0.43 MPa). When using Porcelain Liner M, the results of RelyX ARC (2.94 MPa) were equivalent to the results of self-adhesive cement (3.93 and 2.11 MPa). When using Z-Prime Plus, the results of MaxCem (5.36 MPa) were lower than those of RelyX U200 (9.59 MPa) but equivalent to those of RelyX ARC (6.07 MPa). When using the RelyX ARC, the use of both ceramic primers improved bond strength to zirconia. When using self-adhesive resin cement, Z-Prime Plus improved microshear bond strength values. It can be concluded that, after 24 hours, the highest µSBS results were obtained when using Z-Prime Plus and RelyX U200 self-adhesive cement.

Comparación de la fuerza de adhesión a dentina de cementos de autograbado vs grabado total / Comparison of bond strength to dentin of self-etching cements vs total etching

Los sistemas cementantes han mejorado notablemente, los objetivos que persiguen los nuevos cementos es que la adhesión sea duradera y conseguir siempre que sea posible una interface cerrada con un sellado perfecto. Se han podido desarrollar nuevas técnicas y nuevos materiales de cementación que han ido perfeccionando la unión del material restaurador al diente. En el presente estudio se compara la fuerza de adhesión a dentina de cementos de autograbado y cementos de grabado total para comprobar los efectos positivos en el grabado de la dentina. Para el estudio se utilizaron dos cementos a base de resina (RelyX U200 Clicker 3M y RelyX Ultimate 3M). Se encapsularon 40 molares en acrílico en dos grupos de 20 muestras para la aplicación de dos sistemas cementantes de autograbado (grupo 1) y de grabado total (grupo 2), respectivamente, se desgastaron hasta descubrir la dentina; siguiendo las especificaciones del fabricante se colocó el cemento en cada grupo, y después se sometieron a pruebas de cizalla en una máquina de ensayo universal Instron. La medida expresada en megapascales (MPa) fue: grupo 1 = 7.5569 y grupo 2 = 12.6444. En este caso fueron analizados dos grupos, tomándose la primera significancia bilateral. Se realiza la prueba en t de Student, con 95% de intervalo de confianza en la diferencia, demostrando así que el cemento RelyX Ultimate 3M tiene mayor fuerza de adhesión que el cemento RelyX U200 Clicker 3M. Nuestra investigación fue factible y llegamos a nuestro propósito, en el cual comprobamos la mayor adhesión de cementos de grabado total, los cuales son sometidos a un previo tratamiento del diente (AU)

Influence of diode laser and warm air drying on the shear bond strength of Lithium di-silicate to Dentin. An in-vitro study / Influência do laser de diodo e da secagem com ar quente na resistência ao cisalhamento do Di-silicato de Lítio a dentina. Um estudo in-vitro

Objective: The current study aimed to evaluate the effect of diode laser irradiation (980 nm) and warm air drying (50°C) on shear bond strength between Lithium di-silicate (IPS e.max; Ivoclar) and human dentin using both (Etch & Rinse) adhesive, Adper™ Single Bond 2 (3M ESPE) and (Self-etch) adhesive, Single Bond UniversalTM(3M ESPE) before adhesive polymerization. Material and Methods: 54 sound lower molars were sectioned to obtain flat dentinal surfaces. Specimens were divided into 2 equal groups (n=27): Group 1 (ER) and Group 2 (SE) according to bonding approach. Each subgroup was subdivided according to dentin surface treatment into 3 equal subgroups (n=9): Control (Co), Diode laser irradiation (L) and Warm air drying (W). All specimens were adhesively cemented to IPS e.max® CAD discs using RelyX™ Ultimate Clicker™(3M ESPE) resin cement. Samples were then subjected to pre-loading in a thermodynamic manner. All samples were tested for shear bond strength using computer-controlled material testing machine. Data analysis was performed using two-way (ANOVA) (p< 0.05) followed by pair-wise Tukey's post-hoc tests. Results: In (SE) group, the subgroup (W) had the highest shear bond strength values followed by (Co) subgroup and the least was (L) subgroup with statistically significant difference. As for (ER) group, the subgroup (W) had the highest shear bond strength values followed by (Co) subgroup and the least was (L) subgroup with no statistically significant difference. Conclusion: Warm air drying for (SE) bonding approach increased shear bond strength of Lithium di-silicate to human dentin and can be introduced as a new effective protocol.(AU)

Objetivo: o objetivo do estudo atual é avaliar o efeito da radiação do laser de diodo (980nm) e secagem de ar quente (50°C) na resistência ao cisalhamento entre dissilicati de Lítio (IPS e.max; Ivoclar) e a dentina humana usando ambos modelos de adesivos (condicionamento total) Adper™ Single Bond e (auto-condicionante) Single Bond Universal™ (3M ESPE), Single Bond UniversalTM (3M ESPE) antes da fotopolimerização. Material e Métodos: 54 segundos molares inferiores foram selecionados para obter superfícies dentinárias planas. Os espécimes foram divididos em 2 grupos iguais (n=27): grupo 1 (ER) e grupo 2 (SE) de acordo com protocolo de adesividade. Cada grupo foi subdividido de acordo com o tratamento de superfície dentro de 3 subgrupos iguais (n=9): Controle (co), irradiação com laser de diodo (L) e secagem com ar quente (W). Todos os espécimes foram adesivamente cimentados a discos de IPS emax CAD usando RelyX Ultimate Clicker (3M ESPE) cimento resinoso. As amostras foram então submetidas a pré-carregamento de forma termodinâmica. Todas as amostras foram testadas para resistência a cisalhamento usando máquina de teste de materiais controlados por computador. A análise de dados foi realizada usando ANOVA dois fatores (p<0.05) seguindo por testes de Tukey pareado como test post-hoc. Resultados: No grupo (SE), o subgrupo (W) apresentou maiores valores de resistência ao cisalhamento seguindo o subgrupo (Co) é o menor foi o subgrupo (L) com diferença estatisticamente significativa. Já para o grupo (Er), o subgrupo (W) apresentou os maiores valores de resistência ao cisalhamento seguido do grupo (Co) e o menor foi o subgrupo (L) sem diferença estatisticamente significante. Conclusão: a secagem com ar quente para a abordagem de adesividade (Se) aumentou a resistência ao cisalhamento do dissilicato de lítio à dentina humana e poderia ser introduzido como um novo e eficaz protocolo(AU)

Bond strength of different orthodontic brackets produced with different materials and fabrication methods / Resistência de união de bráquetes ortodônticos produzidos com diferentes materiais e métodos de fabricação

Objective: The aim of this study was to evaluate the effects of material and processing methods on the bond strength of orthodontic brackets. Material and Methods: Five types of brackets were tested: Conventional metallic (CM), metallic sandblasted (SB), ceramic (C), polycarbonate (PC), and metallic fabricated by melting injection molding (MIM). Shear bond strength (SBS) was conducted to check bond strength of the brackets bonded to bovine teeth (n=10/group), and tensile bond strength (TBS) (20 brackets/group) to check bracket retention to bonding material (n=20/group). Both, SBS and TBS were conducted with 1mm/min crosshead speed in a universal testing machine. Bond strength was calculated in Megapascal (MPa) based on force (N) and bracket area (mm 2). Data normality was verified, and One-way ANOVA was the statistical test with Tukey post-hoc (α=0.05). Results: SB and MIM presented higher SBS compared to C, PC, and CM (p<0.05). SB and MIM also presented significantly higher TBS compared to CM and PC (p<0.05). However, MIM was not different of C for TBS. Conclusion: The type of material and method of fabrication are determinant factors that affect bond strength of orthodontic brackets and melting injection molding (MIM) is a remarkable technology to improve brackets retention during the orthodontic treatment. (AU)

Objetivo: O objetivo deste estudo foi avaliar os efeitos dos materiais e métodos de processamento na resistência de união de bráquetes ortodônticos. Material e Métodos: Cinco tipos de bráquetes foram testados: Convencionais metálicos (CM), metálicos jateados (SB), cerâmico (C), policarbonato (PC), e metálico fabricado por injeção de metal fundido em molde (MIM). A resistência de união ao cisalhamento (SBS) foi conduzida para verificar a resistência de união dos bráquetes aderidos a dentes bonivos (n=10/grupo) e a resistência à tração (TBS) (20 bráquetes/grupo) para verificar a retenção do bráquete ao material adesivo (n=20/grupo). SBS e TBS foram conduzidas com relação carga/velocidade de 1mm/min em uma máquina de ensaios universal. A resistência de união foi calculada em Megapascal (MPa) com base na força (N) pela área do bráquete (mm 2). A normalidade dos dados e a estatística foi realizada utilizando One-way ANOVA e Tukey post-hoc (α=0.05). SB e MIM apresentaram os maiores valores de SBS comparados com C, PC e CM (p<0.05). Resultados: SB e MIM também apresentaram valores significativamente maiores de TBS comparados com CM e PC (p<0.05). Contudo, os valores de TBS para o grupo MIM não foram significativamente diferentes de C. Conclusão: O tipo de material e o método de fabricação são fatores determinantes que afetam a resistência de união de bráquetes ortodônticos e a injeção de metal fundido em molde (MIM) é uma tecnologia relevante para melhorar a retenção dos bráquetes durante o tratamento ortodôntico. (AU)

Effectiveness of different orthodontic adhesives and a universal bonding resin on the bond strength of brackets to different ceramics / Eficácia de diferentes adesivos ortodônticos e uma resina de ligação universal na resistência adesiva de bráquetes à diferentes cerâmicas

Objective: The aim of this study was to evaluate the effectiveness of different adhesives on the shear bond strength (SBS) of brackets bonded to different ceramic materials. Material and Methods: Fifty disk-shaped specimens were produced from lithium disilicate (IPS e.max CAD) and monolithic zirconia (Cercon) materials. Each specimen was polished with a three-step diamond polishing system. The polished ceramic surfaces were conditioned with universal bonding resin (Assure Plus) without pre-treatment, except for two specimens. Central brackets were bonded onto different ceramic specimens with different adhesives as follows: group 1: conventional adhesive onto the lithium disilicate; group 2: one-step adhesive onto the lithium disilicate; group 3: conventional adhesive onto the monolithic zirconia; group 4: one-step adhesive onto the monolithic zirconia. After thermal cycling, the specimens were subjected to the SBS test. The adhesive remnant index (ARI) scores were also recorded to evaluate bond failure type. Kruskal­Wallis and Mann-Whitney U tests were used for statistical analysis. Results: There were statistically significant differences among the SBS values (p˂0.05). The monolithic zirconia group with universal bonding resin and conventional orthodontic adhesive demonstrated the highest SBS value (6.34 MPa) and ARI scores. The lithium disilicate group showed the lowest SBS value (2.17 MPa) with the same protocol. No adhesive remained on the lithium disilicate specimens. Conclusion: One-step adhesive and universal bonding resin combination should not be considered as an alternative for lithium disilicate and monolithic zirconia restorations. Conventional adhesive and universal bonding resin application can be effective on non-pretreated ceramic surfaces during orthodontic bonding (AU)

Objetivo: o objetivo deste estudo foi avaliar a eficácia de diferentes adesivos na resistência ao cisalhamento (SBS) de bráquetes colados a diferentes materiais cerâmicos. Material e métodos: Cinquenta espécimes em forma de disco foram produzidos a partir de materiais de dissilicato de lítio (IPS e.max CAD) e zircônia monolítica (Cercon). Cada amostra foi polida com um sistema de polimento de diamante de três passos. As superfícies cerâmicas polidas foram condicionadas com resina de ligação universal (Assure Plus) sem pré-tratamento, exceto para dois corpos-de-prova. Bráquetes centrais foram colados em diferentes corpos de prova cerâmicos com diferentes adesivos da seguinte forma: grupo 1: adesivo convencional sobre dissilicato de lítio; grupo 2: adesivo de uma etapa sobre o dissilicato de lítio; grupo 3: adesivo convencional sobre zircônia monolítica; grupo 4: adesivo de uma etapa sobre a zircônia monolítica. Após a ciclagem térmica, os corpos-de-prova foram submetidos ao teste SBS. Os escores do índice de remanescente adesivo (ARI) também foram registrados para avaliar o tipo de falha de adesão. Os testes U de Kruskal-Wallis e Mann-Whitney foram usados para análise estatística. Resultados: Houve diferenças estatisticamente significativas entre os valores de SBS (p˂0,05). O grupo de zircônia monolítica com resina de colagem universal e adesivo ortodôntico convencional demonstrou o maior valor de SBS (6,34 MPa) e escores de ARI. O grupo de dissilicato de lítio apresentou o menor valor de SBS (2,17 MPa) com o mesmo protocolo. Nenhum adesivo permaneceu nas amostras de dissilicato de lítio. Conclusão: A combinação de adesivo de uma etapa e resina de ligação universal não deve ser considerada como uma alternativa para restaurações de dissilicato de lítio e zircônia monolítica. A aplicação de adesivo convencional e resina de colagem universal podem ser eficazes em superfícies de cerâmica não pré-tratadas durante a colagem ortodôntica (AU)

Comparative Study of the Shear Bond Strengths and Bracket Failure Rates of Two Orthodontic Adhesive Systems

Abstract Objective: To evaluate and compare the shear bond strengths (SBS) and bracket failure rates (BFR) of orthodontic brackets bonded with Light Cure adhesive against those bonded with Self Cure adhesive. Material and Methods: The study had in vitro and in vivo parts. In the in vitro part to determine SBS of Light Bond(LB)(R) and Rely.a.Bond(RB)(R) adhesives used in bonding brackets to 88 extracted teeth, each adhesive type was used to bond 44 brackets. The clinical study was conducted to determine the BFR of the LB(R) and RB(R) adhesives by bonding 256 teeth using each adhesive type. A standardized bonding procedure was followed in both the in vitro and in vivo parts of the study. Data were analyzed using frequency, percentage, mean, independent t-test, chi-square, and Pearson Correlation statistics. A p-value of ≤ 0.05 was considered significant. SPSS version 21.0 was used to analyze the data generated. Results: There was a significantly higher mean SBS 10.6MPa for LB(R) adhesive than the 7.0MPa of the RB(R) adhesive. In the in vivo study, (LB)(R) had a greater but not significant BFR of 9.0% than RB(R) (8.0%). No significant relationship existed between the SBS of either adhesive type (as determined in vitro) and their BFR in vivo. Conclusion: Higher SBS of LB(R) did not translate to less BFR in the clinic, nor did a lower SBS of RB(R) translate to more BFR in the clinic (AU).

Determination of Shear Bond Strength of Nanocomposite to Porcelain and Metal Alloy

Abstract Objective: To compare porcelain and metal repair done with both nanocomposite and conventional composite. Material and Methods: A total of 30 cylinders were fabricated from Porcelain (I), Porcelain fused to metal (II), and metal (III) substrate each. Control group (A) was bonded with conventional micro-hybrid composite and experimental group (B) was bonded with nanocomposite in a 2 mm thickness. All specimens were thermocycled and stored in distilled water at 37 °C for 7 days. A universal testing machine was used to measure the Shear bond strength (SBS). The difference between bond strengths of the groups was compared using an independent t-test. Results: In all three groups, the SBS was higher in the experimental group as compared to the control group. The use of nanocomposite of metal alloy presented maximum shear bond strength, followed by samples of porcelain fused to metal and finally porcelain, showing the lowest values of SBS. Conclusion: Porcelain and alloys bonded with nanocomposite exhibit enhanced adhesiveness as well as aesthetic and mechanical properties. This subsequently would translate into providing higher clinical serviceability and durability and hence a cost-effective and accessible repair option for human welfare (AU).